Click for original picture
Legal status confirmed
Brand:aa
Product detail:
Applications of RTV-2 silicone for shoe sole mold
RTV-2 silicone is suited for shoe mold, simple products, sand casting mold making, shoe mold by pouring way.
Description of RTV-2 silicone for shoe sole mold
Shoe sole mold making silicone rubber is a two-component material, consisting of Part A base silicone and Part B CA30 curing agent, cures at room temperature by a condensation reaction. These materials can be cast into the cured silicone mold: shoe mold making, sand casting etc..
Features of RTV-2 silicone for shoe sole mold
| Item No. | RTV3010 |
| Color | white |
| Curing agent | CA30 |
| Mixing ratio | 100:2 |
| Mixed viscosity | 10000-11000 cps |
| Pot life | 5-10 Minutes |
| Curing time | 4-6 Hours |
| Hardness | 10-13 Shore A |
| Tear Strength | 18 N/mm |
| Tensile Strength | 2.8 MPA |
| Shrinkage | 0.3% |
| Elongation at break | 550% |
| Methods of molding | Pouring |
How to make the silicone shoe sole mold?
The surface of the original should be clean and free of loose material. If your products with thin flower patterns, and especially with porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.
Mixing
Please weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container. Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until the CA30 completely dispersed in the base. Hand or mechanical mixing can be used, but do not for an extended period of time or allow the temperature to exceed 35C(95F). Mix suitably small quantities to ensure thorough mixing of base and curing agent.
It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.
Pouring the mixture and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours(or faster by different mixing ratio or room temperature),we advice you de-mold after 24 hours ,it is will improve the replicate times of silicone mold.
STORAGE
When stored at or below 30 C(85F) in the original unopened containers, Silicone rubber Base and CA30 Curing agent have a usable life of 9 months from the date of production.
Should you have any question, please feel free to contact Ms Julie.
Skype: julieszmc
MSN: julieszmc(at)hotmail(dot)com