RTV2 Silicone Rubber for Concrete Mold Making

Brand:aa

Product detail:

Introduction of RTV2 Silicone Rubber for Concrete Mold Making 

 

RTV2 Silicone Rubber for Concrete Mold Making is a kind of two-component material, that is the moldmaking silicone rubber is made up of Part A base silicone and Part B CA30 curing agent. The mixed Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction,and the become a siliconer rubber mold that can be used for objects reproduction.These  RTV2 silicone molds can be cast into different material for your target objects.The pouring material can be plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...

 

Specifications of MC RTV-2 Silicone Rubber

 

Room Temperature Vulcanization

Equipped with REACH certificate

Professional technician with rich experience

4% catalyst offers for free of charge

Silicone hardness range: 10-60 shore A

High duplicating silicone molds

 

Characteristics of RTV2 Silicone Rubber for Concrete Mold Making 

 

1. Good flow ability and long working time

2. Medium hardness

3. High tear and tensile strength

4. Easy de-mould from complex replica parts

5. Acid and alkali-resistance

6. Low linear shrinkage

 

Applications of RTV2 Silicone Rubber for Mold Making 

 

RTV-2 silicone rubber can be applied in many objects mold making, since the RTV-2 silicone has good flow ability and medium hardness, and the silicone can cure at room temperature, thus it's a good material for duplication.

 

RTV-2 Silicone rubber can be used for artificial stone mold making. For example, RTV2030, RTV2066 and RTV2088 silicone.

 

RTV-2 Silicone rubber can be applied in candle and soap mold making, such as RTV215 and RTV218 silicone.

 

RTV-2 Silicone rubber can be used for plaster mold making, such as RTV2025, RTV2028 and RTV2030 silicone.

 

RTV-2 Silicone rubber can be applied in the field of shoe sole mold making, for example, RTV3010 and RTV3015 silicone.

 

RTV-2 Silicone rubber can be used for prototyping and electronic potting.

 

RTV2 Silicone Rubber for Concrete Mold Making can be applied in the reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. Etc.

 

 

 

Instructions of Making Silicone Mould 

 

1. Make sure the surface of the original is clean and free of loose material. 

2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.

3. Stir Part A base silicone before use thoroughly , as filler separation may occur upon prolonged storage.

4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base. 

5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original

6. De-mold after 24 hours ,it is will improve the replicate times of silicone mold.

Note:It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

 

Shortage of RTV2 Silicone Rubber for Concrete Mold Making 

 

When the RTV2 Silicone Rubber for Concrete Mold Making is stored at or below 30 °C(85 °F) in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production. After 12 months,please use a stirring mill to stir Part A silicone for some minutes, then the silicone can be use again, no influence for other characteristics.

 

FOQ of RTV-2 Silicone Rubber for Mold Making

  

Why does the RTV liquid silicone rubber for molding have few mold making times?

 

 The silicone rubber mold has few molding times is due to follwoing reasons: adding too much silicone oil which will destroy the molecular of silicone rubber; making the mold for small and fine detailed products with higher hardness silicone rubber which is easy to break; making the mold for large products with soft silicone rubber which will reduce the tensile and tear strength of the mold, and the mold will have deformation. Thus, we should take the proper silicone rubber to make the mold for suitable products

 

  

The information above is just for reference, if you're interested or have any questions, please feel free to contact Nicole: