Weave-lock finished fiberglass fabrics
The weave-lock treatment stiffens the fabric slightly to reduce the amount of fraying during fabrication. The weave-lock finished fiberglass fabric enables the user to cut, sew and punch holes more effectively.
Main applications:
-Hullboard.
-Welding blankets
-Fire doos/Fire curtains
-Other fire control systems
DESCRIPTION |
| |||
TGF880-AC225-3008 is a medium weight texturized fiberglass fabric, acrylic weave set finish- high add-on, provide good hand, minimal dust, and ease of application. It’s used for flexible expansion joint, removable jackets, welding protection and other types of fire control systems. | ||||
| ||||
BASE FABRIC | Base fabric style No. TGF880 | |||
| (Metric) | (English) | Test methods | |
Weave | 4 harness satin | Crowfoot |
| |
Yarn |
|
|
| |
Warp | ET9 480 tex | ETG 8.6 |
| |
Weft | ET9 480 tex | ETG 8.6 |
| |
Construction |
|
|
| |
Warp | 10 ± 0.6 ends/cm | 25 ± 2 ends/inch | ASTM D 3775-96 | |
Weft | 8 ± 0.5 picks/cm | 20 ± 1 picks/inch | ASTM D 3775-96 | |
Weight | 880 ± 40 g/m2 | 25.8 ± 1.2 oz/yd2 | ASTM D3776-96 | |
Thickness | 1.0 ± 0.1 mm | 0.039 ± 0.005 inch | ASTM D1777-96 | |
|
| |||
COATED FABRIC | Coating style No. AC225-3008 | |||
Coating | Acrylic weave-set finish on both sides, high add-on. | |||
Weight | 910 ± 40 g/m2 | 27 ± 1.2 oz/yd2 | ASTM D3776-96 | |
Thickness | 1.05 ± 0.1 mm | 0.043 ±0.005 inch | ASTM D1777-96 | |
Color | Black |
| ||
Temp resistance | 5500C | 10000F |
| |
Colors for choice: