Applications:

Electro dialysis.

Electroforming.

Cathodic Protection.

Electrochemical Sensing.

Electro winning and Refining of metals.

Electrolytic Regeneration of chromic acid.

Electroplating for precious and base metals.

Electrolytic recovery for precious and base metals.

Electrolytic Production of Sodium Hypochlorite.

Electro synthesis of Inorganic & Organic chemicals.

Specifications:

Description PTA PNA MMOA

PH Level: (between) 1.0-12.0 1.0-10.0 1.0-12.0

Pt / mixed oxide layer thick 1.5-20.0 1.5-15.0 8.0

Fluorides content (max) 50mg/l 500mg/l 50mg/l

Allowable current (max) 50A/dm2 100A/dm2 50A/dm2

Anodes available in mesh, plate, sheet, rod, wire, Tube or custom-built

PTA: Pt. Titanium PNA: Pt. Niobium MMOA: Mixed Metal Oxide Coated

Advantages:

Low weight.

Good current resistance.

Long operating life: maintenance free.

Economical, due to low platinum requirements.

High dimensional stability and load resistance.

Highly suitable as auxiliary anodes of complex geometrical shapes.

Availability:

Pt. plated Titanium anode 1250mm x 1000mm

Pt. plated Nb / Moly anodes 900mm x 500mm

Plating thickness minimum 1.5 µ and maximum 20 µ

Recommendations:

Plated and Non-plated hanging hook, frame / band.

Platinum (Pt) Plated Titanium (Ti) is for electrolytes without fluoride.

Platinum (Pt) Plated Niobium (Nb) for electrolytes having fluoride and where better conductivity is needed.

Nb has 3 times better conductivity than Ti.

Platinum plated Niobium is for Sulphuric acid chromium plating bath operated at Current Density (CD) 75 A per dm² or more.

Platinum plated Molybdenum used as container for oxidizing slag at high temperature to measure the viscosity of steel making slag at temperatures of 1500 - 1650°C.

Both plated and Non-plated hanging hook, frame / band.