35% fiberglass high-tempetature and lower nylon
The common nylon resin will be much lower in tenacity in low temperature and dry environment ,leading to easily break,while our nylon get a excellent tractility,even in the low temperature and dry environment.Our nylon is widely used in electric tools,atmobile outer parts and ski,sled and other outdoor products.
Data Sheet for 35% fiberglass high-tempetature and lower nylon (TW50BG7)
| Properties | Test Conditions | Test standard | Unit | TW50BG7 |
| Mechanical properties | ||||
| Tensile Strength | 5mm/min | ISO527-1/2 | Mpa | 198 |
| Elongation at break | 5mm/min 50mm/min | ISO527-1/2 | % | 2.5 |
| Flexural Modulus | 2mm/min | ISO178 | Mpa | 10600 |
| Flexural Strength | 2mm/min | ISO178 | Mpa | 290 |
| Charpy Impact Strength | 23°c | ISO179/1eA | KJ/M2 | 17 |
| Charpy Unnotched Impact Strength | 23°c | ISO179/1eA | KJ/M2 | 80 |
| Thermal Properties | ||||
| Melting Temperature | DSC.10K/min | ISO3146 | °c | 280 |
| HDT A | 1.8Mpa | ISO75 | °c | 248 |
| HDT B | 0.45Mpa | ISO75 | °c | 265 |
| Electrical Properties | ||||
| Surface Resistivity | IEC60093 | Ohm | 1/.01 | |
| Volume Resistivity | Testsotution A | IEC60093 | ohm*cm | 10/0.1 |
| Physical Properties | ||||
| Density | 23°c | ISO1183 | g/cm3 | 1.4 |
| Damp Absorption | 23°c 50%.r.h | ISO62 | % | |
| Water Absorption | 23°c saturtion | ISO62 | % | 0.39 |
| Radial Shrinkage | flow | ISO294-4 | % | 0.9 |
| Transverse Shrinkage | transverse | ISO294-4 | % | 0.2 |
| Flame retardant | ||||
| Flammability Test | 1.6/3.0mm | UL94 | HB | |
| Material Description | 35% fiberglass high-temperature nylon |
Photo:
Appliation: Our nylon is widely used in electric tools,atmobile outer parts and ski,sled and other outdoor products.